How To Determine If Your Pistons Are Still Good

Evaluating Used Pistons:
How to Determine if Your Pistons Are Still Good.

Co-ordSport would like to share this information with you.

Gamblers are a different breed. There’s a point where they seem to know when a bluff has gone too far, when it’s time to fold their hand and live to fight another day. The art of building racing and high performance engines involves often pushing engines near their limit. The difference is a good engine builder knows how to stack the odds in his favor. Is reusing pistons worth the risk? Here’s how to make an informed decision.

Freshening up an engine has always been a game of careful disassembly and evaluating the components for wear, followed by a series of judgment calls that balance the cost of new parts against further pushing the veterans. Evaluating pistons takes a practiced eye, but there are several checking points that any engine builder can use to help make the right call.

While some kinds of damage may be obvious, there can be other telltales like wrist pins that require excessive force to remove – clear evidence of piston distortion.

We spoke with JE Pistons’ Gregg Suyenaga regarding what to look for with seasoned pistons. Physical damage such as piston-to-valve contact might induce other issues that you may not realize. For example, we had a chance to inspect a small-block Chevy that had suffered valve-to-piston contact issue on one piston. At first, it appeared the piston had survived the damage otherwise unscathed except for a mark left by the valve. But when we attempted to remove the floating pin, it had to be driven out of the piston with a hammer and punch. Contact on the piston crown had altered the piston shape enough to distort the pin bore. While honing the pin bore might have restored the piston, the builder simply chose to not take the risk and just replaced the piston.

Inspect used pistons carefully for visual cues like damaged ring lands or deep scoring in the skirt area. (As Shown Below)

If any full-floating piston is disassembled from the rod, JE also recommends using new round wire clips or Spirolocks. Installing these clips or locks is not easy which is why using new ones is a good idea. Some engine builders chamfer the ends of the round wire clips to prevent gouging the wrist pin bore.

Clips or Spirolocks should not be reused. Replacing them is cheap insurance against failure for these hard-to-install components.

Short of contact damage, normal wear evaluation on a performance piston should start with a quick visual piston skirt check followed by measuring at the piston’s guide point. The guide point is the area on the skirt where the diameter is the largest. On JE pistons, this is generally located 0.500-inch above the bottom of the skirt, but you should verify this with the piston’s individual part number.

When measuring piston diameter, make sure to do it at the point specified by the manufacturer for accurate results.

If the engine builder recorded the original piston diameter, a simple comparison will reveal any changes. It’s possible to see pistons with partially collapsed skirts from detonation or physical contact problems that otherwise visually check out fine. A minor change in piston-to-wall clearance can be considered normal, but changes in the piston-to-wall clearance of more than 0.002-inch should be considered a good excuse for a change. Keep in mind that 4032 pistons run a much tighter piston-to-wall clearance compared to 2618 alloy pistons, so the clearances will be different.

Perhaps the place where wear can cost the most can be found in the top ring groove. All rings use cylinder pressure behind the top ring to increase sealing load on the ring. This demands a somewhat tight axial or vertical clearance between the ring groove and the piston. JE’s axial clearance recommendations will vary with specific pistons, but a generic clearance of 0.001 to 0.002-inch is acceptable. This can be measured with a feeler gauge between the top of the ring and the groove. Worn ring lands can also exhibit more clearance toward the outboard edge of the groove, creating a bell mouth effect, which will negatively affect ring seal.

Ring groove clearance is another measure of the health of a used piston.

Beyond worn ring grooves, high output engines, especially supercharged or turbocharged engines, tend to load the top ring with far more cylinder pressure. Micro-welding is a term used to describe the transfer of small amounts of aluminum from the ring land to the ring surface. This material transfer tends to reduce the axial clearance and may in fact contribute to sticking the ring in the groove. Clues that may point to lost ring seal due to mirco-welding include increased blow-by and lost power.

Piston rings are designed with vertical clearance so that they can freely move within the groove, and are induced to move by the angle of the cross-hatch pattern honed into the cylinder wall. Micro-welding can reduce piston ring movement, which also contributes to reduced sealing efficiency. When the rings are removed from the piston, evidence of micro-welding will be pitting in the lower surface of the ring groove and the lower horizontal face of the ring itself. This will be more prevalent with pistons that place the top ring closer to the piston crown as this increases the temperature the ring must face.

Pitting in the lower surface of the top ring groove and the lower face of the ring itself is a sign of micro-welding, and signals that it’s time to replace the pistons and rings.

If either the piston or the top ring exhibit evidence of micro-welding, the only solution is a new set of pistons and rings. Avoiding a re-occurrence of this issue involves careful initial ring break-in that allows establishing early wear patterns that remove the tallest peaks early before maximum cylinder pressure is applied.

As mentioned earlier, wrist pin and pin bore condition are also areas that should be carefully inspected. If the wrist pin appears distressed through discoloration or it is difficult to remove from either the rod or the piston, that’s a clear indication the pin not only should be replaced, but also to use that as a clue pointing toward changes that will minimize that problem in the future. According to Suyenaga, if the pin bore is worn more than 0.002-inch, JE recommends the piston be replaced.

A pin bore gauge is the best way to check for excessive wear in this area.

Other potential failure points include inspecting the rings to ensure the ring end gaps, especially the top ring, has not butted. If you find the top or even second ring end is highly polished, this is a good sign that the ring end gap was too tight. This may only occur under highly loaded conditions when additional heat expands the ring. But this insufficient ring clearance will immediately bind the ring in the groove, causing excessive wear and the possibility of a broken ring land. The solution is either to open up the gap slightly, or replace the rings with a new set with additional clearance.

Only the best-equipped engine builders will have the tools needed to determine if a piston has suffered excessive annealing.

For engines that see extended use at high engine speeds such as endurance or circle track applications, there can be a concern over loss of tensile strength due to heat cycle annealing, or a softening of the original material’s heat treatment. The only way to know for sure is to send the pistons out for a Rockwell or Brinnell hardness test, which can be expensive.

Discoloration can also be an indicator of a piston that has reached the end of its service life.

Suyenaga suggests that careful inspection of the back side of the piston crown is a great indicator of piston condition. If the back side of the piston crown is discolored black, dark purple, blue or any dark color, this is an obvious warning sign that the piston crown has experienced an overheated condition and has likely gone soft. This can lead to eventual failure, so swapping out these pistons would be the smart call. This also indicates that perhaps the air-fuel ratio or ignition timing needs to be more closely scrutinized. Conversely, a tan or light brown color on the piston back side is acceptable, usually caused by combustion heat oxidizing a portion of the crankcase oil.

We’ve just hit the most popular places for potential piston distress, but if you have a question about a JE piston beyond what we’ve covered here, JE technicians can help answer any questions. It doesn’t have to be a game of chance when it comes to piston survival, especially when you can load the positive statistics on your side of the horsepower equation.

Thank you.

For more information on JE pistons and parts please call +44121 6616263 or email us at sales@coordsport.com

 

In order to provide you with the best possible service, Co-ordSport uses cookies. By clicking on any link on this site you accept cookies. For more information check us out Privacy policy

The cookie settings on this website are set to "allow cookies" to give you the best browsing experience possible. If you continue to use this website without changing your cookie settings or you click "Accept" below then you are consenting to this.

Close